Niloy F30
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niloy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G6XtO9_Niloy-F30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC-PBT alloy reinforced with 30% glass fibre, high stiffness and hardness. Good resistance against chemical agents, high dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.050 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 90.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus 3 | 6500 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.20 mm | 120 | J/m | |
| 23°C, 3.20 mm | 200 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 138 | °C | ASTM D648 |
| Vicat Softening Temperature | 145 | °C | ASTM D1525 5 |
| CLTE - Flow (23 to 55°C) | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Relative Permittivity (1 MHz) | 3.20 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® 21SPF | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| NEMCON H PA DP117/X3 | Ovation Polymers Inc. | PEEK | NEMCON H |
| NORYL™ ZM3640 resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| LubriOne™ AT-000/05T 2S | PolyOne Corporation | Acetal (POM) Copolymer | LubriOne™ |
| MACOMASS PP MM-PP GF 20 | MACOMASS Verkaufs AG | PP, Unspecified | MACOMASS PP |