Machine Cast MC-145 A/B
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | Machine Cast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G61l6v_Machine-Cast-MC-145-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MC-145 A/B is a two-component urethane casting compound that can be used with meter-mix-dispense equipment. This product is a safe, easy-to-handle, room temperature mixing and curing system that does not contain TDI, MDI, MDA, or MOCA. MC-145 A/B is relatively insensitive to typical environmental moisture and will make good void-free parts without the problems that some conventional urethane systems exhibit. Because of this product's exceptional toughness and abrasion resistance, castings made with MC-145 A/B are particularly suitable for the mineral process and metal forming industries. Product Uses:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.07 | g/cm³ | |
| -- | 1.08 | g/cm³ | ASTM D792 |
| -- 2 | 1.10 | g/cm³ | |
| Shrinkage | 0.60 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time | 5.0 | min | |
| Work Time 3(25°C) | 4.0 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time | 3.0 to 5.0 | day |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 43 to 47 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 82.7 | MPa | ASTM D412 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 20.7 | MPa | ASTM D412 |
| Tensile Elongation (Yield) | 290 | % | ASTM D412 |
| Tear Strength | 47.3 | kN/m | ASTM D624 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 95, Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity | Brookfield | ||
| 25°C 4 | 1650 | cP | |
| 25°C 5 | 3800 | cP | |
| 25°C | 2800 | cP | |
| Demold Time (25°C) | 30 to 60 | min | |
| Post Cure Time (74°C) | 16 | hr |
| Note Message | |
|---|---|
| 1 . | Part B |
| 2 . | Part A |
| 3 . | 100g mass |
| 4 . | Part B |
| 5 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® QE546AT | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| NEFTEKHIM PE 4052V (52418) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| PENTAMID B SK H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| Sylvin 8280-65 Brown 7434 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| apilon 52® FA-56E | API SpA | TPU-Polyester | apilon 52® |