CERTENE™ LDF-820A
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G5aOqi_CERTENE-LDF-820A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LDF-820A is a certified prime resin specially designed for production of laminates and coating Blown films. LDF-820A features easy processability and very good color stability. Films exhibit good mechanical properties, resistance to pinholling and excellent heat seal performance. Applications include lamination film, extrusion coating, expandable foam and as carrier resin for color com pounding. Maximum recommended drawdown is 0.5 mils. LDF-820A contains no slip and no antiblock. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm | 228 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm | 275 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 11.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 11.0 | MPa | ASTM D882 |
| MD : Break, 25 µm | 18.0 | MPa | ASTM D882 |
| TD : Break, 25 µm | 18.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 330 | % | ASTM D882 |
| TD : Break, 25 µm | 600 | % | ASTM D882 |
| Dart Drop Impact (25 µm) | 50 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 350 | g | ASTM D1922 |
| TD : 25 µm | 120 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm) | 75 | ASTM D2457 | |
| Haze (25.4 µm) | 5.5 | % | ASTM D1003 |
| Additional Information |
|---|
| Film Specimen: 1.0 mils (25 µm) film, melt temperature 300-340°F (150-170°C), blow-up-ratio 2.25 :1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 170 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2770 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Sylvin 8996-75 FU White 1295 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VITAMIDE® AB76NT6501 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| KEBAFORM® C 130.2 | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| Sylvin 8203-55 Green 3172 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |