TITANLENE® LDF 266YZ
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Lotte Chemical Titan (M) Sdn. Bhd. |
| Trademark: | TITANLENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G5PMPu_TITANLENE-LDF-266YZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TITANLENE® LDF 266YZ is a Low Density Polyethylene material. It is available in Asia Pacific for film extrusion. Important attributes of TITANLENE® LDF 266YZ are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 150 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 150 µm, Blown Film | 177 | MPa | |
| 1% Secant, TD : 150 µm, Blown Film | 206 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 150 µm, Blown Film | 22.6 | MPa | |
| TD : Break, 150 µm, Blown Film | 18.6 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 150 µm, Blown Film | 480 | % | |
| TD : Break, 150 µm, Blown Film | 570 | % | |
| Dart Drop Impact (150 µm, Blown Film) | 600 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® Gel TP3607 | Momentive Performance Materials Inc. | Silicone Rubber, RTV-2 | Silopren® |
| Sylvin 2958-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TOTAL Polypropylene PPH 3827WZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Cellophane™ 335WS | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Politen® G3LS10 | ITEN INDUSTRIES | Polyester Alloy | Politen® |