GERMAMID 6.6 GF 25 V0
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Kunststoff-Kontor-Hamburg GmbH |
| Trademark: | GERMAMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G4rS7c_GERMAMID-6-6-GF-25-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GERMAMID 6.6 GF 25 V0 is a Polyamide 66 (Nylon 66) material filled with 25% glass fiber. It is available in Europe. Primary attribute of GERMAMID 6.6 GF 25 V0: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 to 1.1 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 1.4 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 40 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 250 | °C | ISO 75-2/A |
| Melting Temperature | 255 | °C | |
| Thermal Conductivity | 0.24 | W/m/K | ISO 8302 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ming Dih EPS S3 | Ming Dih Group Corporation | PS (EPS) | Ming Dih EPS |
| TECHNO ABS H593 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Nordbak High Temp. Wear Compound | Loctite® | Epoxy | Nordbak |
| Edgetek™ AT-30GF/000 NC005 S-ROHS | PolyOne Corporation | Acetal (POM) Copolymer | Edgetek™ |
| LUVOCOM® 1105-7194/GY | LEHVOSS Group | PEEK | LUVOCOM® |