| Category: | Nylon 66+Nylon 6I/6T , Polyamide 66 + PA 6I/6T |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G4ntBQ_AKROLOY-PA-GF-50-8-black-4173-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROLOY® PA GF 50 8 black (4173) is a 50% glass fibre reinforced polyamide blend with very high stiffness and strength, as well as reduced moisture absorption, modified for the respective application. Applications are components with tight dimensional tolerances even under high mechanical load, especially in drinking water industry. It is a very cost effective alternative for zinc- and aluminium diecast alloys. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.59 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 3.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 17000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 260 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 17000 | MPa | ISO 178 |
| Flexural Stress 2 | 400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 17 | kJ/m² | |
| 23°C | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 120 | kJ/m² | |
| 23°C | 110 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 242 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 183 | °C | ISO 75-2/C |
| Melting Temperature 3 | 250 | °C | DIN EN 11357-1 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content | 50 | % | ISO 1172 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu RTV KE-1833 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| TEDUR® L 9116-1 | ALBIS PLASTIC GmbH | PPS | TEDUR® |
| Staramide RF006SXS | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| DynaChar™ 2435-TH | Polymer Dynamix | TPU, Unspecified | DynaChar™ |
| KetaSpire® KT-880 GF30 | Solvay Specialty Polymers | PEEK | KetaSpire® |