INSULGEL 90
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULGEL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G4mBqT_INSULGEL-90.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSULGEL 90 is a room temperature curing, transparent, epoxy gel in which the gel number actually equals the hardness. INSULGEL 90 is low viscosity and does not normally require vacuum de-gassing to void-free castings and imbedments. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 6.89 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 75 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 6.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.23 | W/m/K | |
| Service Temperature | 105 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.50 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.020 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 25 | ||
| Shelf Life (25°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 1 | Amber | ||
| -- 2 | Clear/Transparent | ||
| Density | |||
| -- 3 | 0.958 | g/cm³ | |
| -- 4 | 1.05 | g/cm³ | |
| Viscosity | ASTM D2393 | ||
| -- 5 | 0.10 | Pa·s | |
| -- 6 | 0.20 | Pa·s | |
| -- 7 | 0.30 | Pa·s | |
| Curing Time (25°C) | 72 | hr | |
| Pot Life (25°C) | 60 to 90 | min |
| Note Message | |
|---|---|
| 1 . | Part B |
| 2 . | Part A |
| 3 . | Part B |
| 4 . | Part A |
| 5 . | Part B |
| 6 . | Mixed |
| 7 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GS40-60 42LH-N | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| LNP™ LUBRICOMP™ RP004S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| POLYCASA® ACRYL G 88 E | Polycasa | Acrylic (PMMA) | POLYCASA® ACRYL |
| Hostacom M4 U42 LW92607 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| PETILEN F2-26TO | PETKIM Petrokimya Holding A.S. | LDPE | PETILEN |