HIVOREX BL6200
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | HIVOREX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G4Ucoi_HIVOREX-BL6200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HIVOREX BL6200 is produced by slurry process technology. This resin is ideally suited for use in blow molding application. HIVOREX BL6200 is designed to offer high speed processability, good ESCR. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.958 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.35 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (F50) | 400 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 55 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 27.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | 1320 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 123 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Beamset 1461 | Arakawa Chemical Industries, Ltd. | Acrylic, Unspecified | Beamset |
| BP RPP 4010 T NAT | Buckeye Polymers, Inc. | PP, Unspecified | BP |
| Flexalloy® 9300-70 | Teknor Apex Company | PVC Elastomer | Flexalloy® |
| Garaflex™ E 89-086-C3 NAT NF LCF-R | AlphaGary | TPE | Garaflex™ E |
| Iupital® F40-03 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |