ENVIROLON® ENV1266G33-NAT
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | ENVIROPLAS®, Inc. |
| Trademark: | ENVIROLON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G4Axei_ENVIROLON-ENV1266G33-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Injection Molding Grade, 33% Fiberglass Reinforced, Natural, Lubricated, RoHS Compliant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 - 0.60 | % | ASTM D955 |
| Ash Content | 33 | % | ASTM D5610 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 165 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 6860 | MPa | ASTM D790 |
| Flexural Strength | 193 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 91 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 246 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 93.3 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 249 - 282 | °C | |
| Middle Temperature | 260 - 288 | °C | |
| Front Temperature | 271 - 304 | °C | |
| Nozzle Temperature | 271 - 304 | °C | |
| Mold Temperature | 65.6 - 110 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Injection Pressure High, adjust to just above a short shot. Back Pressure Utilize only if necessary to provide uniform melt. Fill Rate Fast, depending on part surface appearance. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® A3L HP | BASF Corporation | Nylon 66 | Ultramid® |
| ACCUTECH™ CP0437M40L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Estane® 58300 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Geon™ Vinyl Dry Blend E1500 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Dry Blend |
| KOPLA PP KPT1010 | KOPLA Co., Ltd. | PP, Unspecified | KOPLA PP |