HAIPLEN EP50 C10 Z1
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G49DZI_HAIPLEN-EP50-C10-Z1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HAIPLEN EP50 C10 Z1 is a polypropylene copolymer (PP Copoly) product, which contains 50% calcium carbonate filler. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.75 - 0.85 | % | ASTM D955 |
| Transverse flow | 0.75 - 0.85 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 30.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 20 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2200 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 25 | J/m | ASTM D256 |
| 0°C | 35 | J/m | ASTM D256 |
| 23°C | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 130 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 151 | °C | ASTM D1525, ISO 306/A50 1 1 |
| -- | 75.0 | °C | ASTM D1525, ISO 306/B50 2 2 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| Notched Izod Impact Strength , ISO 180, 23°C: 50 J/mNotched Izod Impact Strength , ISO 180, -20°C: 25 J/mNotched Izod Impact Strength , ISO 180, 0°C: 35 J/mMelt Mass-Flow Rate , ISO 1133, 230/2.16 kg: 4 to 10 g/10minMelt Mass-Flow Rate , ASTM D1238, 230/2.16 kg: 4 to 10 g/10minCTI IEC 112, IEC 60112, Method A: >600 V |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 200 - 220 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 速率 A (50°C/h), 压 力1 (10N) |
| 2 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1200 S-80A | RTP Company | TPU-Polyester | RTP |
| Santoprene™ 8281-65MED | ExxonMobil Chemical | TPV | Santoprene™ |
| Sumikon® PM-6431 | Sumitomo Bakelite Co., Ltd. | Phenolic | Sumikon® |
| Magnobond 75 | Magnolia Plastics, Inc. | Epoxy | Magnobond |
| Macromeric® 0110-108 BK | Saco Polymers | CPE | Macromeric® |