Nirion F10
| Category: | PC , Polycarbonate |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Nirion |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G453aP_Nirion-F10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate reinforced with 10% glass fibre, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.30 | % | |
| Equilibrium, 23°C, 50% RH | 0.12 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 75.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus 3 | 3600 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.20 mm | 80 | J/m | |
| 23°C, 3.20 mm | 120 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 145 | °C | ASTM D648 |
| Vicat Softening Temperature | 148 | °C | ASTM D1525 5 |
| CLTE - Flow (23 to 55°C) | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.10 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 9.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature | 850 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL STAR™ AF 218 V35 BLACK 21N | Solvay Engineering Plastics | Nylon 66 | TECHNYL STAR™ |
| SLOVAMID® 66 GF 15 T 6 TS | Plastcom | Nylon 66 | SLOVAMID® 66 |
| DOWLEX™ 2355 | The Dow Chemical Company | EPE | DOWLEX™ |
| LNP™ LUBRICOMP™ RFN16 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ LUBRICOMP™ |
| LNP™ LUBRICOMP™ KL003 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |