DESLOY™ DSC901G2
| Category: | PC , Polycarbonate |
| Manufacturer: | DESCO Co., Ltd. |
| Trademark: | DESLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G3gOiN_DESLOY-DSC901G2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Descriptions: DESLOY™ DSC901G2 is PC(Polycarbonate) Glass Fiber 10% filled reinforced resin. It has good electrical property and weatherability. Applications: DESLOY™ DSC901G2 is applied to Electronic & Electrical Parts which request good electrical property and dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 61.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | % | ASTM D638 |
| Flexural Modulus | 2450 | MPa | ASTM D790 |
| Flexural Strength | 95.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 130 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 115 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 275 - 280 | °C | |
| Middle Temperature | 280 - 290 | °C | |
| Front Temperature | 280 - 290 | °C | |
| Nozzle Temperature | 280 - 290 | °C | |
| Processing (Melt) Temp | 280 - 290 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C |
| Injection instructions |
|---|
| Speed: 40 to 70%Pressure 1st: 30 to 60%Pressure 2nd: 30 to 60Holding Pressure: 10 to 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Carboprene® 1040AV NATURALE | SO.F.TER. SPA | PP Homopolymer | Carboprene® |
| Estane® 58215 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Elastron® D D400.D62.B | Elastron USA, Inc. | SBS | Elastron® D |
| Karina IVORY PVC COMPOUND 853-35/ 1-DY-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Durez® 37042 | SBHPP | Phenolic | Durez® |