Order Products : sales@su-jiao.com

UMERIT® 613A

Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	UBE America, Inc.
Trademark:	UMERIT®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	G3bVh7_UMERIT-613A.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
UBE super polyethylene UMERIT® are ethylene alpha-olefin copolymers produced using metallocene catalyst by gas phase process. The metallocene catalytic method results in superior physical properties by being able to acquire any targeted molecular structures. Therefore UMERIT®613A offer various excellent properties. -Superior transparency and low temperature flexibility -The surface of processed products is free from stickiness and cloud due to the elimination of low molecular weight elements -High reliability products are guaranteed due to superior mechanical properties and high ESCR properties

Message

UBE super polyethylene UMERIT® are ethylene alpha-olefin copolymers produced using metallocene catalyst by gas phase process. The metallocene catalytic method results in superior physical properties by being able to acquire any targeted molecular structures.
Therefore UMERIT®613A offer various excellent properties.
-Superior transparency and low temperature flexibility
-The surface of processed products is free from stickiness and cloud due to the elimination of low molecular weight elements
-High reliability products are guaranteed due to superior mechanical properties and high ESCR properties

General Information
Features	Copolymer High Clarity High ESCR (Stress Crack Resist.) Low Temperature Flexibility
Appearance	Clear/Transparent
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Density	0.913	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR)	30	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance (F50)	20.0	hr	ASTM D1693

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	50		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	30.0	MPa	ASTM D638
Tensile Elongation (Break)	850	%	ASTM D638
Flexural Modulus	230	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	87.0	°C	ASTM D1525
Melting Temperature	113	°C

Resin Grade	Manufacturer	Category	Trademark
TPUCO® TPUI-E95	Taiwan PU Corporation	TPU-Polyester	TPUCO®
WPP PP PPH4CF-2	Washington Penn Plastic Co. Inc.	PP Homopolymer	WPP PP
NORYL GTX™ GTX989 resin	SABIC Innovative Plastics Europe	PPE+PS+Nylon	NORYL GTX™
Garaflex™ E 4771-A8 NAT OR-1 LCF	AlphaGary	TPE	Garaflex™ E
Lupol® ED1045D	LG Chem Ltd.	TPO (POE)	Lupol®