Generic PEEK - Glass Fiber
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G3MY4p_Generic-PEEK---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PEEK - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.36 - 1.65 | g/cm³ | ASTM D792 |
| 23°C | 1.37 - 1.62 | g/cm³ | ISO 1183 |
| Spiral Flow | 8.50 - 41.4 | cm | |
| Molding Shrinkage | |||
| Flow : 23°C | 0.19 - 0.81 | % | ASTM D955 |
| Transverse flow : 23°C | 0.56 - 2.0 | % | ASTM D955 |
| 23°C | 0.15 - 0.93 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.099 - 0.16 | % | ASTM D570 |
| 23°C, 24 hr | 0.098 - 0.10 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.14 - 0.40 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 103 - 124 | ASTM D785 | |
| Durometer Hardness (23°C) | 86 - 88 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 4830 - 15000 | MPa | ASTM D638 |
| 23°C | 5900 - 13100 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 2.07 - 178 | MPa | ASTM D638 |
| Yield, 23°C | 124 - 175 | MPa | ISO 527-2 |
| Fracture, 23°C | 122 - 183 | MPa | ASTM D638 |
| Fracture, 23°C | 85.6 - 191 | MPa | ISO 527-2 |
| 23°C | 102 - 187 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.0 - 3.1 | % | ASTM D638 |
| Yield, 23°C | 1.4 - 3.5 | % | ISO 527-2 |
| Fracture, 23°C | 0.87 - 4.5 | % | ASTM D638 |
| Fracture, 23°C | 1.7 - 5.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 4100 - 11400 | MPa | ASTM D790 |
| 23°C | 4810 - 12100 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 153 - 286 | MPa | ASTM D790 |
| 23°C | 138 - 273 | MPa | ISO 178 |
| Compressive Stress (23°C) | 41.0 - 250 | MPa | ISO 604 |
| Coefficient of Friction | 0.28 - 0.33 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 - 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 29 - 61 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 42 - 140 | J/m | ASTM D256 |
| 23°C | 4.2 - 13 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 420 - 970 | J/m | ASTM D256 |
| 23°C | 30 - 65 | kJ/m² | ISO 180 |
| Instrumented Dart Impact (23°C) | 13.5 - 14.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 298 - 330 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 240 - 338 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 260 - 323 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 237 - 315 | °C | ISO 75-2/A |
| Continuous Use Temperature | 248 - 256 | °C | ASTM D794 |
| Vicat Softening Temperature | 300 - 325 | °C | ISO 306 |
| Melting Temperature | 343 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | |||
| Flow | 2.2E-5 - 2.9E-5 | cm/cm/°C | ASTM D696 |
| Flow | 3.6E-6 - 4.9E-5 | cm/cm/°C | ASTM E831 |
| Flow | 1.1E-5 - 3.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.8E-6 - 3.1E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 2.0E-6 - 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.30 - 0.40 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 5.1E+4 - 4.8E+15 | ohms | ASTM D257 |
| -- | 1.0E+12 - 2.6E+13 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 5.1E+2 - 1.9E+16 | ohms·cm | ASTM D257 |
| 23°C | 8.4E+14 - 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 6.9 - 23 | kV/mm | ASTM D149 |
| 23°C | 21 - 24 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.40 - 4.20 | ASTM D150 | |
| 23°C | 3.10 - 3.50 | IEC 60250 | |
| Dissipation Factor (23°C) | 1.0E-3 - 5.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 150 - 200 | V | IEC 60112 |
| Insulation Resistance (23°C) | 1.0E+12 - 2.5E+14 | ohms | IEC 60167 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | 210 - 850 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 119 - 151 | °C | |
| Drying Time | 3.0 - 7.0 | hr | |
| Dew Point | -28.9 | °C | |
| Rear Temperature | 365 - 366 | °C | |
| Middle Temperature | 370 - 386 | °C | |
| Front Temperature | 394 - 395 | °C | |
| Nozzle Temperature | 370 | °C | |
| Processing (Melt) Temp | 371 - 391 | °C | |
| Mold Temperature | 179 - 191 | °C | |
| Injection Pressure | 86.2 - 104 | MPa | |
| Back Pressure | 0.500 - 0.517 | MPa | |
| Screw Speed | 55 - 80 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PEEK - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NaturePlast PEVI 001 | NaturePlast | HDPE | NaturePlast |
| Akulon® Ultraflow K-FG6 | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |
| AKROMID® A3 ICF 20 S1 black (5057) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Tunhe PET TH103 | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PET | Tunhe PET |
| NILAMID® XS1 GF50 | Nilit Plastics | Nylon, Unspecified | NILAMID® |