RAMOFIN PPH316G4
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMOFIN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G2zT1R_RAMOFIN-PPH316G4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% GLASS-FIBER REINFORCED, HIGH HEAT STABILIZED POLYPROPYLENE FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.20 - 0.50 | % | ASTM D955 |
| -- | 0.20 - 0.50 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3900 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 85.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 4100 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 115 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| 23°C | 9.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 143 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 137 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 165 | °C | ISO 11357-3, ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 - 220 | °C | |
| Middle Temperature | 200 - 225 | °C | |
| Front Temperature | 205 - 230 | °C | |
| Mold Temperature | 30.0 - 65.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Holding Pressure | 35.0 - 70.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultraform® S 1320 0021 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Yanshan PE 1F7B | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| ASI POLYPROPYLENE 3353-01 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| Karina BLACK PVC COMPOUND E-CAK 60-48/1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pearlthane® MB-9010 | Lubrizol Advanced Materials, Inc. | TPU, Unspecified | Pearlthane® |