Toyolac® 920 555
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Plastics (Malaysia) Sdn. Bhd. |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G2RF8f_Toyolac-920-555.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac® 920 555 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific or Europe. Important attributes of Toyolac® 920 555 are:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2540 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 1 | 48.0 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 2 | 20 | % | ASTM D638 |
| Break | 17 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 3 | 2160 | MPa | ASTM D790 |
| -- 4 | 2260 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 5 | 74.0 | MPa | ASTM D790 |
| -- 6 | 77.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 12.7 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 83.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 77.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3000 µm) | 88.0 | % | ASTM D1003 |
| Haze (3000 µm) | 2.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 3.0 mm/min |
| 6 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT4700-01A | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| GAPEX® RPP20EA10BK | Ferro Corporation | PP Homopolymer | GAPEX® |
| EPS Silver® SR500R | INEOS Styrenics International SA | PS (EPS) | EPS Silver® |
| Hifax TRC 298P | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Luran® S Q440 | Styrolution | ASA | Luran® S |