Bergamid™ A700 G20 HW UF
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G206tS_Bergamid-A700-G20-HW-UF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bergamid™ A700 G20 HW UF is a Polyamide 66 (Nylon 66) product filled with 20% glass fiber. It can be processed by extrusion or injection molding and is available in Africa & Middle East, Asia Pacific, Europe, or North America. Typical application: Outdoor Applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density 1 | 1.34 | -- | g/cm³ | DIN 53479 |
| Outdoor Suitability (Black) | f1 | -- | UL 746C |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 8000 | 7200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 115 | -- | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | -- | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 245 | -- | °C | ISO 306/A50, ISO 306/B50 |
| Melting Temperature (DSC) | 261 | -- | °C | ISO 3146 |
| RTI Elec | UL 746 | |||
| 0.750 mm | 125 | -- | °C | |
| 1.50 mm | 125 | -- | °C | |
| 3.00 mm | 125 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 100 | -- | °C | |
| 1.50 mm | 110 | -- | °C | |
| 3.00 mm | 120 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.750 mm | 105 | -- | °C | |
| 1.50 mm | 115 | -- | °C | |
| 3.00 mm | 125 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (CTI) | PLC 1 | -- | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.400 mm, ALL | V-0 | V-0 | ||
| 0.750 mm, ALL | V-0 | V-0 | ||
| 1.50 mm, ALL | V-0 | V-0 | ||
| 3.00 mm, ALL | V-0 | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.400 mm | 960 | -- | °C | |
| 0.800 mm | 960 | -- | °C | |
| 1.60 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.800 mm | 725 | -- | °C | |
| 1.60 mm | 725 | -- | °C | |
| 3.00 mm | 750 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Holding Pressure | 40.0 to 90.0 | MPa |
| Note Message | |
|---|---|
| 1 . | ±0.03 g/cm³ |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC 6907 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 1600 TFE 20 | RTP Company | PAS | RTP |
| Moplen EP300M | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| NYLOY® UB-0010N G50L1N | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| Latistat 63-08 | LATI S.p.A. | Nylon 6 | Latistat |