Moplen HP526J
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G1uLF8_Moplen-HP526J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen HP526J is a polypropylene homopolymer designed for the production of biaxially oriented polypropylene films (BOPP). The product is suitable for metallizable film, both as monolayer film and in coextruded structures. It contains a standard processing stabilisation but does not contain any slip, antiblocking agents and is Calcium Stearate free. Moplen HP526J offers good optical, excellent & highly consistent processing and very good film profile. Typical applications are BOPP packaging film and sheet for Solid Phase Thermoforming. Moplen HP526J is suitable for food contact. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 34.0 | MPa | |
| Break | 23.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 12 | % | |
| Break | > 500 | % | |
| Flexural Modulus | 1450 | MPa | ISO 178 |
| Coefficient of Friction (Dynamic) | 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Tangent (20 µm) | 3000 | MPa | Internal Method |
| Tensile Strength - MD 1(Break, 20 µm) | 260 | MPa | ASTM D882 |
| Tensile Elongation - MD 2(Break, 20 µm) | 85 | % | ASTM D882 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 85.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 154 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 91 | MA 17021 | |
| Haze (20.0 µm) | 0.30 | % | MA 17031 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| polyvic® E-1822-PV 31 | Unipack Plasindo | PVC, Unspecified | polyvic® |
| Quadrant EPP TIVAR® Extrended Wear | Quadrant Engineering Plastic Products | UHMWPE | Quadrant EPP |
| Salflex 623TIM | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| SEETEC LDPE XJ710 | Lotte Chemical Corporation | LDPE | SEETEC LDPE |
| Shin-Etsu Elastomer FE-361U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |