SABIC® PP 576S
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G1s8ZQ_SABIC-PP-576S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PP 576S is a PP homopolymer grade that has good flow properties, excellent demoulding properties and a narrow molecular weight distribution. Products made from SABIC® PP 576S typically have low warpage, high stiffness in combination with moderate impact strength at room temperature and a high gloss. SABIC® PP 576S is typically used in caps & closures and thin wall packaging both in food and non-food segments, and appliances. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 19 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 | |
| Shore Hardness (Shore D) | 71 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1850 | MPa | ASTM D638 |
| -- | 1800 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 37.0 | MPa | ASTM D638 |
| Yield | 37.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 9.0 | % | ASTM D638 |
| Yield | 9.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 25 | J/m | ASTM D256A |
| 23°C | 3.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 90.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 65.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 60.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 152 | °C | ASTM D1525, ISO 306/A120 6 6 |
| -- | 94.0 | °C | ASTM D1525, ISO 306/B120 7 7 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP TPO TPO-2563AS UV Black | Washington Penn Plastic Co. Inc. | TPO | WPP TPO |
| ALTECH® PC C 2010/121 GF10 IM UV | ALBIS PLASTIC GmbH | PC | ALTECH® PC |
| Devlon PTFE | Devol® Engineering Polymers | TP, Unspecified | Devlon |
| Elastollan® A 1154 DN | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |
| Plaslube® Actrn | Techmer Engineered Solutions | Acetal (POM) Homopolymer | Plaslube® |