Propafilm™ RK140
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G1iFI5_Propafilm-RK140.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Heat Sealable Anti-Mist Coated Film Biaxially oriented polypropylene (BOPP) film coated with two aqueous dispersions of polyvinylidene chloride (PVdC) copolymer. RK100/120/140 are recommended for use as a single web in the salad industry. Particularly suited for medium to large packs on formfill-seal machines. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | Internal Method | ||
| Flow : 121°C, 1 min | 4.0 | % | |
| Flow : 129°C, 1 min | 7.0 | % | |
| Across Flow : 129°C, 1 min | 4.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.25 | ||
| vs. Itself - Static | 0.25 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 3600 | µm | |
| Seal Strength 1 | 0.15 | N/mm | Internal Method |
| Seal Initiation Temperature 2 | 90.6 to 146 | °C | Internal Method |
| Oxygen Permeability (25°C, 0% RH) | 0.63 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate (38°C, 90% RH) | 4.5 | g/m²/24 hr | ASTM F1770 |
| Yield | 29.1 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 100 | ASTM D2457 | |
| Haze 3 | 3.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 265°F; 1sec; 15lb/in² |
| 2 . | 2secs; 15psi |
| 3 . | Wide angle; 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT HI2304 | Sincerity Australia Pty Ltd. | PC+PBT | Sindustris PBT |
| Abstron SE-22M | Bhansali Engineering Polymers Limited | ABS | Abstron |
| ALTECH® PA6 A 2035/109 GF35 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Borstar® HE6068 | Borealis AG | HDPE | Borstar® |
| Globalene® ST611K | Lee Chang Yung Chemical Industry Corp. | PP Random Copolymer | Globalene® |