Generic TPU Alloy
| Category: | TPU Alloy , Thermoplastic Polyurethane Elastomer Alloy |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G1e7yr_Generic-TPU-Alloy.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic TPU Alloy This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 to 1.23 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 45 to 98 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 0.483 to 7.76 | MPa | ASTM D638 |
| Taber Abrasion Resistance (23°C) | 18.8 to 65.6 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain, 23°C) | 1.60 to 14.7 | MPa | ASTM D412 |
| Tensile Strength (Yield, 23°C) | 28.4 to 54.1 | MPa | ASTM D412 |
| Tensile Elongation (Break, 23°C) | 350 to 690 | % | ASTM D412 |
| Tear Strength (23°C) | 49.0 to 147 | kN/m | ASTM D624 |
| Compression Set | 21 to 44 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -53.6 to -28.0 | °C | DSC |
| Vicat Softening Temperature | 87.9 to 147 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TechnoElast 9075 | TechnoCompound GmbH | SEBS | TechnoElast |
| DENIFORM 0037 | Vamp Tech | Acetal (POM) Copolymer | DENIFORM |
| Gallonprene® GP210-4002L | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Lupol® HI5204H | LG Chem Ltd. | TPO | Lupol® |
| MAJORIS HG313X - 8229 | AD majoris | PP, Unspecified | MAJORIS |