LNP™ LUBRICOMP™ RAL22 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G1af5N_LNP-LUBRICOMP-RAL22-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* RAL22 is a compound based on Nylon 66 resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RAL-4022 Product reorder name: RAL22 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 1.9 | % | |
| Across Flow : 24 hr | 2.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.72 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3450 | MPa | ASTM D638 |
| -- | 3500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 81.5 | MPa | ASTM D638 |
| Break | 79.2 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 8.1 | % | ASTM D638 |
| Break | 9.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2960 | MPa | ASTM D790 |
| -- | 3500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 113 | MPa | ASTM D790 |
| -- | 117 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.55 | ||
| vs. Itself - Static | 0.46 | ||
| Wear Factor - Washer | 13.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 2 | 5.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 740 | J/m | ASTM D4812 |
| 23°C 3 | 49 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.40 | J | ASTM D3763 |
| -- | 1.42 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 249 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 198 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 193 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 7.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.4E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 8.1E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 8.3E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Latamid 66 H2 G/25-V0KB | LATI S.p.A. | Nylon 66 | Latamid |
| LEXAN™ EXL1112 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| OxyVinyls® 240 | OxyVinyls, LP | PVC Homopolymer | OxyVinyls® |
| Plaslube® J-1300/30/TF/15 | Techmer Engineered Solutions | PPS | Plaslube® |
| Petrothene® XL07420B | LyondellBasell Industries | Polyolefin, Unspecified | Petrothene® |