UMG ABS® VW702S
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | UMG ABS, Ltd. |
| Trademark: | UMG ABS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G1R47i_UMG-ABS-VW702S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UMG ABS® VW702S is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific or North America for injection molding. Important attributes of UMG ABS® VW702S are:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 30.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (23°C) | 0.50 to 0.70 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 95 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2000 | MPa | ISO 527-2 |
| Tensile Stress (23°C) | 40.0 | MPa | ISO 527-2 |
| Flexural Modulus 1(23°C) | 2100 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 59.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 10 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 77.0 | °C | ISO 75-2/Af |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.50 mm | 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 6.0 | hr | |
| Rear Temperature | 150 to 190 | °C | |
| Middle Temperature | 170 to 210 | °C | |
| Front Temperature | 180 to 220 | °C | |
| Nozzle Temperature | 170 to 210 | °C | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 50.0 to 60.0 | °C | |
| Injection Pressure | 70.0 to 130 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 5.00 to 10.0 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3865A | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| POLYPRO® 5014L ASL015 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| Ebalta MG 804 / Comp. A+B | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| HiFill® PA6 LE BK | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| LubriOne™ AT-000/15T BLACK | PolyOne Corporation | Acetal (POM) Copolymer | LubriOne™ |