Fiberfil® J-68/20/E/SD
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G1OaK7_Fiberfil-J-68-20-E-SD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fiberfil® J-68/20/E/SD is a Polypropylene Copolymer (PP Copolymer) material filled with 20% glass fiber. It is available in North America. Important attributes of Fiberfil® J-68/20/E/SD are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.20 to 0.30 | % | |
| 6.35 mm | 0.30 to 0.40 | % | |
| Water Absorption (24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 4.0 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 3300 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 70.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 136 | °C | |
| 1.8 MPa, Unannealed | 129 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® OM-10176 | Teknor Apex Company | TPE | Monprene® |
| Tarnamid® T- 30 MHLS | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| IROGRAN® A 92 E 4694 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| LUVOCOM® 1850/CF/10/GF/10/BK | LEHVOSS Group | PBT | LUVOCOM® |
| LNP™ THERMOCOMP™ RF00AH compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |