Order Products : sales@su-jiao.com
TRANSMARE® 19HT40-0.002
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G1I6SG_TRANSMARE-19HT40-0-002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 19HT40-0.002 is a 40% standard (gray) talc filled polypropylene homopolymer for injection molding purposes with high stiffness and good flow. Not suitable for light colors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 18 | g/10 min | |
| 230°C/5.0 kg | 80 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 74 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00 mm | 33.0 | MPa | |
| Break, 4.00 mm | 30.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00 mm | 2.5 | % | |
| Break, 4.00 mm | 5.0 | % | |
| Flexural Modulus 1 | 4900 | MPa | ISO 178 |
| Flexural Stress 2 | 53.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.4 | kJ/m² | ISO 179/A |
| Notched Izod Impact Strength (23°C) | 2.5 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 119 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 153 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULABLEND® (PC/ASA) WR 5 UV CA | A. Schulman Europe | ASA+PC | SCHULABLEND® |
| Titacon® TR910 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| ChronoFlex® C 55D | CardioTech International, Inc. | PUR, Unspecified | ChronoFlex® |
| PolyFibra® PF-AED01 | FuturaMat | ABS | PolyFibra® |
| Daelim Po1y® XP9100S | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |