Radilon® A ESL128
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G1Aqlg_Radilon-A-ESL128.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA66 injection moulding grade. Good impact strength. Natural colour |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.09 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 7.6 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2300 | 1350 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 55.0 | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.6 | 30 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 50 | 50 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/eA | |||
| -30°C | 21 | 11 | kJ/m² | ISO 179/eA |
| 23°C | 58 | 110 | kJ/m² | ISO 179/eA |
| Charpy Unnotched Impact Strength | ISO 179/eU | |||
| -30°C | No Break | No Break | ISO 179/eU | |
| 23°C | No Break | No Break | ISO 179/eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 140 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 60.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 210 | -- | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | UL 94 | |
| 1.60 mm | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357-1-3 at a heating rate of 10°C/min.Nominal Tensile Strain at Break, ISO 527: >50% |
| 调节后的 Nominal Tensile Strain at Break, ISO 527: >50% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® H033MG | Reliance Industries Limited | PP Homopolymer | REPOL® |
| Sindustris ABS LXR515 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| BMC 810 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| EPO-TEK® T6065 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| InSphere® 0513FR-P | Synthos S.A. | PS (EPS) | InSphere® |