INEOS LLDPE LL6908AA
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G0qRGe_INEOS-LLDPE-LL6908AA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LLDPE film products Applications: LL6908AA is low-gel polymer suitable for use in blends for geomembrane and geoliner applications. Benefits and Features: LL6908AA is a linear low density polyethylene copolymer containing hexene-1 as the comonomer. It offers the following properties:
If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. We recommend that you consult your INEOS O&P Europe technical representative for further advice on the use of LL6908AA. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.936 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) (190°C/0.325 kg) | 0.90 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Modulus - 1% Secant (38 µm, Blown Film) | 450 | MPa | ISO 1184 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 38 µm, Blown Film | 18.0 | MPa | |
| TD : Yield, 38 µm, Blown Film | 21.0 | MPa | |
| MD : 38 µm, Blown Film | 54.0 | MPa | |
| TD : 38 µm, Blown Film | 36.0 | MPa | |
| Tensile Elongation | ISO 1184 | ||
| MD : Break, 38 µm, Blown Film | 780 | % | |
| TD : Break, 38 µm, Blown Film | 990 | % | |
| Dart Drop Impact (38 µm, Blown Film) | 65 | g | ASTM D1709A |
| Elmendorf Tear Strength 2 | ASTM D1922 | ||
| MD : 38.0 µm | 13.7 | kN/m | |
| TD : 38.0 µm | 127.5 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 121 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 13 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | Conditioned according to ISO 1872/1 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sipolprene® 58210 B | SIPOL S.p.A | TPC-ET | Sipolprene® |
| SOLLAMID A 2750 FV | Krisoll Resinas Plásticas Ltda. | Nylon 66 | SOLLAMID |
| Nylene® BS-700-RA | Custom Resins Group | Nylon 6 | Nylene® |
| Geon™ Vinyl Flexible 90401 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LUVOCOM® 1/GF/30/TF/15/HS/BK | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |