Zytel® HTN 51G35EF BK083
| Category: | PPA , HIGH PERFORMANCE POLYAMIDE RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® HTN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G0Abbg_Zytel-HTN-51G35EF-BK083.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% Glass Reinforced, PPA, High Performance Polyamide Developed for Electrical and Electronics Applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Part Marking Code (SAE J1344) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.47 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.60 | -- | % | |
| Flow | 0.20 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12100 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break) | 220 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.4 | -- | % | ISO 527-2 |
| Flexural Modulus | 11000 | -- | MPa | ISO 178 |
| Flexural Stress | 300 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 57 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 264 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 300 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.8E-5 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 5.7E-5 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 5.3E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 29 | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity (100 Hz) | 4.40 | -- | IEC 60250 | |
| Dissipation Factor (100 Hz) | 0.016 | -- | IEC 60250 | |
| Comparative Tracking Index | 525 | -- | V | IEC 60112 |
| Note Message | |
|---|---|
| 1 . | First Heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Kostrate® EDGE PSG 02 Impact Modifier | Plastic Selection Group, Inc. | TP, Unspecified | Kostrate® EDGE |
| LNP™ KONDUIT™ OX10324 compound | SABIC Innovative Plastics Asia Pacific | PPS | LNP™ KONDUIT™ |
| LUVOCOM® 50/TF/15/GY04 | Lehmann & Voss & Co. | PC | LUVOCOM® |
| Pacrel® 5365N-NA | Nanjing Jinling OPTA Polymer Co., Ltd. | TPE | Pacrel® |
| LEXAN™ 915R resin | SABIC Innovative Plastics | PC | LEXAN™ |