Badamid® T70 CF30
| Category: | Nylon 6/6T , Polyamide 6/6T Copolymer |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fz59Tf_Badamid-T70-CF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% carbon fibre reinforced injection moulding grade with superior mechanical properties, high dimensional stability and electrical conductive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.26 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.3 to 5.3 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.80 to 1.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 22000 | 21000 | MPa | ISO 527-2/1 |
| Tensile Stress 1(Yield, 23°C) | 250 | 245 | MPa | ISO 527-2/50 |
| Tensile Strain 2(Yield, 23°C) | 2.0 | 2.0 | % | ISO 527-2/50 |
| Flexural Stress 3(23°C) | 330 | 320 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 4(23°C) | 10 | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 5(23°C) | 100 | 100 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength 6(23°C) | 10 | -- | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 7 | ||||
| 0.45 MPa, Unannealed | 270 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 270 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 8 | 295 | -- | °C | ISO 3146 |
| Maximum Service Temperature | IEC 216 | |||
| 20000 hrs | 135 | -- | °C | |
| some hours | 260 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 9 | < 1.0E+5 | -- | ohms | IEC 60093 |
| Volume Resistivity 10 | < 1.0E+5 | < 1.0E+5 | ohms·cm | IEC 60093 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 310 to 340 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | 80x10x4 mm |
| 4 . | 80x10x4 mm |
| 5 . | 80x10x4 mm |
| 6 . | 80x10x4 mm |
| 7 . | 110x10x4 mm |
| 8 . | 10 K/min, Compound for moulding |
| 9 . | 80x80x1 mm |
| 10 . | 80x80x1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zytel® 80G33HS1L NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| FERREX® GPP30CS81HB NATURAL | Ferro Corporation | PP Copolymer | FERREX® |
| OPNYL OP66GF43 | Ovation Polymers Inc. | Nylon 66 | OPNYL |
| OTECH PVC PL1001-11 - Riser Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| Sylvin 9067-80 RED 604 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |