Styrolution PS 153F
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Styrolution PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fy4IH8_Styrolution-PS-153F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Styrolution PS 153F is general purpose polystyrene with high heat resistance and good flow properties. Styrolution PS 153F is free of internal lubricants, e.g. zinc stearate. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 7.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | < 0.10 | % | |
| Equilibrium, 23°C, 50% RH | < 0.10 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 150 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3050 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 1.5 | % | ISO 527-2 |
| Flexural Modulus | 3250 | MPa | ISO 178 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Annealed) | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 101 | °C | ISO 306/B120 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.16 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+18 | ohms·cm | IEC 60093 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 280 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1205-90A | RTP Company | TPU-Polyester | RTP |
| PRIMALENE WPP620Q | Southern Polymer, Inc. | LLDPE | PRIMALENE |
| ExxonMobil™ HDPE HMA 018 | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| LNP™ COLORCOMP™ 123RC compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |
| Thermec S™ 4150RC50 | Technical Polymers, LLC | PPS | Thermec S™ |