Cri-Line FKX-719-75
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | Cri-Tech, Inc. |
| Trademark: | Cri-Line |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FxxQKa_Cri-Line-FKX-719-75.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The LS compounds are designed to give part shrinkage (out of the mold) and post-curing operation comparable to a nitrile or similar elastomer. In most cases, tooling changes are not required when switching over to an LS compound. NPC indicates no post cure required to achieve high tensile and modulus values with good compression set and aging characteristics. FKHT is a high temperature resistant, low compression set compound. FKX is a high viscosity, high green strength, black fluorocarbon compound formulated for HAV and / or salt bath curing of O-ring cord and extruded profiles. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.84 | g/cm³ |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 75 |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Stress (100% Strain) | 7.58 | MPa | |
| Tensile Strength | 14.4 | MPa | |
| Tensile Elongation (Break) | 190 | % | |
| Compression Set 1(200°C, 22 hr) | 12 | % |
| Note Message | |
|---|---|
| 1 . | Plied discs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® LSR 3486/50 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| Sinvicomp SFC8200 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Sup-tech CT703 | Shanghai Suptech Engineering Plastics Co. Ltd. | PC+PBT | Sup-tech |
| Kepamid® 2300MRH | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |
| Sylvin 8200-80UV Red 6257 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |