Alathon® M6010SB
| Category: | HDPE, MMW , High Density (MMW) Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FxfspA_Alathon-M6010SB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Alathon M6010SB is a medium molecular weight high density polyethylene homopolymer for use in blown film applications. Typical applications include those with low WVTR requirements. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.958 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | 1.1 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus | ASTM E111 | ||
| MD | 1340 | MPa | ASTM E111 |
| TD | 883 | MPa | ASTM E111 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 27.6 | MPa | ASTM D882 |
| TD : Yield | 32.4 | MPa | ASTM D882 |
| MD : Fracture | 64.1 | MPa | ASTM D882 |
| TD : Fracture | 22.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 600 | % | ASTM D882 |
| TD : Fracture | 400 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 20 | g | ASTM D1922 |
| TD | 600 | g | ASTM D1922 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 199 - 210 | °C |
| Extrusion instructions |
|---|
| 2.2:1 Blow-up-ratio, 60 mil die gap |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 216 BLACK 21 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Tecomid® NBX0 HF75 NL | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| NuSil MED2-6300 | NuSil Technology | Silicone | NuSil |
| CERTENE™ LDF-420A | Muehlstein | LDPE | CERTENE™ |
| Maxxam™ H4 GF30 H black | PolyOne Corporation | PP Homopolymer | Maxxam™ |