Witcom PA6 2009/142
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fxdpyr_Witcom-PA6-2009-142.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Witcom PA6 2009/142 is a polyamide 6 (nylon 6) product that contains a filler. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.20 - 0.40 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 6.3 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 125 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 - 4.0 | % | ISO 527-2 |
| Flexural Modulus | 9000 | MPa | ISO 178 |
| Flexural Stress | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 4.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 200 | °C | ISO 75-2/A |
| CLTE - Flow | 2.7E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Imp (3.00 mm) | 95.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 - 1.0E+5 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | ISO 1210 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 50.0 - 90.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 1.00 | MPa |
| Injection instructions |
|---|
| Screw speed: 0.1 - 0.2 m/sInjection pressure: Keep to a minimumHold pressure: Keep to a minimum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Wire & Cable GA-1046-80E | S&E Specialty Polymers, LLC | PVC, Semi-Rigid | S&E Wire & Cable |
| SEQUEL® 2326 | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| Hanwha Total PP BI45W | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| FUDOWLITE® F5980F | Fudow Co., Ltd. | Phenolic | FUDOWLITE® |
| LNP™ KONDUIT™ OX10324 compound | SABIC Innovative Plastics Asia Pacific | PPS | LNP™ KONDUIT™ |