ENGAGE™ 8003 EL Polyolefin Elastomer is an ethylene-octene copolymer that has excellent flow characteristics and performs well in a wide variety of Wire & Cable elastomer applications. ENGAGE 8003 EL provides superb impact properties and also provides high filler loading capability and outstanding peroxide cure capability. When cross-linked by peroxide, silane, or irradiation, it gives exceptional heat aging, compression set, and weather resistance properties, and may be used to produce high performance electrical insulation and jacketing.

Main Characteristics:

Pellet form

Excellent flow characteristics

High filler loading

Peroxide, silane, and radiation curable

Exceptional heat aging, compression set, and weather resistance when cured

Applications:

Wire and cable

Complies with:

EU, No 10/2011

Japan Hygienic Olefin and Styrene Plastics Association

NSF/ANSI Standard 51-Food Equipment Materials

U.S. FDA 21 CFR 177.1520(c)3.2c

General Information
Uses	Blending Building Wire Insulation Building Wire Jacketing Compounding Low Voltage Insulation Wire & Cable Applications
Agency Ratings	EU No 10/2011 FDA 21 CFR 177.1520(c) 3.2c JHOSPA Unspecified Rating NSF Unspecified Rating
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.885	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.0	g/10 min	ASTM D1238
Mooney Viscosity (ML 1+4, 121°C)	22	MU	ASTM D1646

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness			ASTM D2240
Shore A, Compression Molded	84
Shore D, Compression Molded	31

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus - 100% Secant ¹(Compression Molded)	4.80	MPa	ASTM D638
Tensile Strength ²(Break, Compression Molded)	18.2	MPa	ASTM D638
Tensile Elongation ³(Break, Compression Molded)	640	%	ASTM D638
Flexural Modulus			ASTM D790
1% Secant : Compression Molded	33.7	MPa
2% Secant : Compression Molded	32.6	MPa

Elastomers	Nominal Value	Unit	Test Method
Tear Strength ⁴	61.0	kN/m	ASTM D624

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	-46.0	°C	Internal Method
Vicat Softening Temperature	63.0	°C	ASTM D1525
Melting Temperature (DSC) ⁵	77.0	°C	Internal Method
Peak Crystallization Temperature (DSC)	60.0	°C	Internal Method

Note Message
1 .	510 mm/min
2 .	510 mm/min
3 .	510 mm/min
4 .	Die C
5 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
Vipel® F774-BBC-00	AOC, L.L.C.	Polyester Alloy	Vipel®
DENKA STYROL MW-1-321	Denka Company Limited	PS (GPPS)	DENKA STYROL
Evoprene™ G 3315	AlphaGary	SEBS	Evoprene™ G
ELASTOSIL® M 4511	Wacker Chemie AG	Silicone	ELASTOSIL® M
POLYFLON™ M-112	DAIKIN AMERICA, INC.	PTFE	POLYFLON™