DIC.PPS Z-200
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | DIC Corporation |
| Trademark: | DIC.PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FweTMv_DIC-PPS-Z-200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DIC.PPS Z-200 is a polyphenylene sulfide (PPS) product,. It can be processed by injection molding and is available in North America or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.5 | % | ASTM D955 |
| Transverse flow | 1.7 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ASTM D638 |
| Tensile Strength | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 2600 | MPa | ASTM D790 |
| Flexural Strength | 95.0 | MPa | ASTM D790 |
| Compressive Strength | 70.0 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 150 | J/m | ASTM D256 |
| Unnotched Izod Impact | 2000 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 170 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 110 | °C | ASTM D648 |
| CLTE - Flow (-30 to 100°C) | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 5.0E-3 | ASTM D150 | |
| Arc Resistance | 60.0 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Additional Information |
|---|
| Flexural Elongation @ Break, ASTM D790: NB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 300 - 340 | °C | |
| Middle Temperature | 300 - 340 | °C | |
| Front Temperature | 300 - 340 | °C | |
| Mold Temperature | 120 - 150 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ROPOTEN® T FV-03-223-2 | LUKOIL Bulgaria Ltd. | LDPE | ROPOTEN® T |
| NEOPLAST 180 FT EB | Zylog Plastalloys | TPV | NEOPLAST |
| AKROMID® T1 GF 40 9 black (3499) | AKRO-PLASTIC GmbH | PPA | AKROMID® |
| Karina MBU RED(OP) -E 42/268-FC-HSF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hifax HSBM CB 1158 G C12763 | LyondellBasell Industries | PP Copolymer | Hifax |