Nylene® 9543

Category:	Nylon 612 , Polyamide 612
Manufacturer:	Custom Resins Group
Trademark:	Nylene®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	FwQm9n_Nylene-9543.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

43% glass fiber reinforced heat stabilized nylon 6/12

Good chemical properties and reduced moisture absorption of nylon 6/12 resins while adding glass reinforcement to increase strength and stiffness

Suitable in applications where typical nylon 6 or 6/6 may be unsuitable due to moisture absorption or specific chemical requirements

On Special Order only.

General Information
Filler / Reinforcement	Glass Fiber, 43% Filler by Weight
Additive	Heat Stabilizer
Features	Good Stiffness Good Strength Low Moisture Absorption

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.46	g/cm³	ASTM D792
Molding Shrinkage - Flow	0.10	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (23°C)	165	MPa	ASTM D638
Tensile Elongation (Break, 23°C)	5.0	%	ASTM D638
Flexural Modulus (23°C)	8480	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	110	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	210	°C	ASTM D648
Peak Melting Temperature	224	°C	ASTM D3418

Resin Grade	Manufacturer	Category	Trademark
XENOY™ 1102 resin	SABIC Innovative Plastics	PC+PBT	XENOY™
3M™ Dyneon™ PTFE Compound TF 3105	3M Advanced Materials Division	PTFE	3M™ Dyneon™ PTFE Compound
Elastron® G G101.A30.B	Elastron USA, Inc.	SEBS	Elastron® G
Karina BLACK PVC COMPOUND -E 858-48/ 1-CY-IS-LMP	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
LNP™ THERMOCOMP™ DX06411 compound	SABIC Innovative Plastics	PC	LNP™ THERMOCOMP™