Order Products : sales@su-jiao.com
4LOY® 10E27700
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | 4Plas |
| Trademark: | 4LOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FwEEzg_4LOY-10E27700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4LOY 10E27700 is a Standard Flow 10% PC / 90% ABS PC/ABS |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Across Flow | 0.50 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2400 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 45.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 50 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 20 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 106 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 99.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 105 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 50.0 - 100 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 60 - 80 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201 H | RTP Company | Nylon 66 | RTP |
| Mirakutoran® TPU P890 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Sinvicomp SGH6000D | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| ExxonMobil™ PP7033E2 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| Globalene® ST751 | Lee Chang Yung Chemical Industry Corp. | PP Impact Copolymer | Globalene® |