SCHULAFORM® AF 9
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAFORM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FvqewC_SCHULAFORM-AF-9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aramid fibre filled POM-Compound with improved abrasion resistance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 4.50 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/10) | 132 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 3250 | MPa | ASTM D638 |
| -- | 2900 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | |||
| Yield | 55.0 | MPa | ISO 527-2/1A/50 |
| Break | 56.0 | MPa | ASTM D638 |
| -- | 56.0 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield | 8.5 | % | ISO 527-2/1A/50 |
| Break | 12 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (3.20 mm) | 61 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 156 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 100 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 163 | °C | ISO 306/A50 |
| -- | 147 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | 34 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 625 | °C | |
| 3.00 mm | 625 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 650 | °C | |
| 3.00 mm | 650 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® CB5108H | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Copolymer | POLYPRO® |
| TOTAL Polystyrene Crystal 1160 | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |
| AKROMID® B3 GF 50 RM-M black (3146) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Karina NATURAL PVC COMPOUND -E TR-75701-25/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ULTEM™ 1010 resin | SABIC Innovative Plastics | PEI | ULTEM™ |