Order Products : sales@su-jiao.com
Arnitel® PL581
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Arnitel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FuzwIx_Arnitel-PL581.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Arnitel® PL581 is a Thermoplastic Copolyester Elastomer (TPC-ET) material. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Arnitel® PL581: Flame Rated. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.8 | % | |
| Flow | 1.7 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 2.5 | % | |
| Equilibrium, 23°C, 50% RH | 0.40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 3 sec) | 53 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 210 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 31.0 | MPa | |
| 5.0% Strain | 9.20 | MPa | |
| 10% Strain | 13.2 | MPa | |
| 50% Strain | 16.5 | MPa | |
| 100% Strain | 17.0 | MPa | |
| Nominal Tensile Strain at Break | 400 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 16 | kJ/m² | |
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 15 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 100 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 105 | °C | ISO 306/B50 |
| Melting Temperature 1 | 218 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.1E-4 | cm/cm/°C | |
| Transverse | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 21 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 4.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.040 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (1.60 mm) | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 220 to 240 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SAP-6104X60 | SHIN-A T&C | Acrylic, Unspecified | SHIN-A |
| Telcar® OBC 4475A | Teknor Apex Company | TPE | Telcar® |
| SUMILITE® PL-1102 | Sumitomo Bakelite Co., Ltd. | Phenolic | SUMILITE® |
| Novalloy-B B5722 | PlastxWorld Inc. | ABS+PBT | Novalloy-B |
| AKROMID® A4 1 natural (3716) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |