LG ABS SH610S
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fug6Y3_LG-ABS-SH610S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Excellent Surface, High Impact Application Bag, Miscellous |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 94 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 35.3 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield, 3.20mm | > 5.0 | % | ASTM D638 |
| Fracture, 3.20mm | 35 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1960 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 56.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 410 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 350 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm 5 | 92.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 6.40mm 6 | 87.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 94.0 | °C | ASTM D1525 7 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Cylinder Zone 1 Temp. | 180 - 210 | °C | |
| Cylinder Zone 2 Temp. | 190 - 230 | °C | |
| Cylinder Zone 3 Temp. | 200 - 250 | °C | |
| Cylinder Zone 4 Temp. | 200 - 250 | °C | |
| Adapter Temperature | 200 - 250 | °C | |
| Melt Temperature | 200 - 250 | °C | |
| Die Temperature | 200 - 250 | °C |
| Extrusion instructions |
|---|
| Top RollStack Temperature: 70 to 100°CMiddle RollStack Temperature: 70 to 90°CBottom RollStack Temperature: 60 to90°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | 4.6kg |
| 6 . | 18.6kg |
| 7 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuman PS 810 | Shuman Plastics, Inc. | PS (HIPS) | Shuman PS |
| NuSil R2-6755 | NuSil Technology | Silicone | NuSil |
| Biograde® C 6509 CL | FKuR Kunststoff GmbH | Biodeg Polymers | Biograde® |
| Exelene® HDPE 20000 | Montachem International, Inc. | HDPE | Exelene® HDPE |
| Hostaform® LW15EWX | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |