INDURE™ X210A
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | INDURE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FuEHG1_INDURE-X210A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Indure X210A engineered polyolefin material is designed for large, molded-in-color automotive exterior applications that require good scratch-and-mar characteristics, ductile impact properties at low temperatures and processability |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.990 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 23 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 20.7 | MPa | ASTM D638 |
| Yield, 4.00 mm 2 | 21.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | |||
| 23°C 3 | 1380 | MPa | ASTM D790 |
| 4.00 mm 4 | 1400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Impact (-30°C) | 1.89 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 108 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 150x10x4 mm |
| 3 . | 1.3 mm/min |
| 4 . | 80x10x4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makroblend® UT235 M | Covestro - Polycarbonates | PC+PET | Makroblend® |
| POLYLAN AG10AP | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| REPOL® B250EG | Reliance Industries Limited | PP Impact Copolymer | REPOL® |
| Moplen RP340H | LyondellBasell Industries | PP Random Copolymer | Moplen |
| LNP™ THERMOCOMP™ WF006H compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |