Durethan® B 35 FA 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS Corporation |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FtgBom_DurethanB35FA000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, non-reinforced, extrusion, medium viscosity, slip agent |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.14 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (235°C/2.16 kg) | 7.00 | -- | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 10 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 130 | 40.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2800 | 800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 75.0 | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 4.0 | 25 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 20 | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2600 | 700 | MPa | ISO 178/A |
| Flexural Stress (3.5% Strain, 23°C) | 90.0 | 20.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 2(23°C) | 5.0 | 8.0 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, ES, 18-030 | -- | ISO 1874 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 5.0 | 50 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact (-30°C) | 7.0 | 7.5 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 150 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 50.0 | -- | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 40.0 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B120 |
| Melting Temperature 3 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+14 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 30 | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 23°C, 100 Hz | 3.90 | 18.0 | IEC 60250 | |
| 23°C, 1 MHz | 3.50 | 4.00 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | UL 94 | |
| 1.60 mm | HB | -- | UL 94 | |
| Oxygen Index 4 | 24 | -- | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 10°C/min |
| 4 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL NY66-IM1-(color)H | Polymer Resources Ltd. | Nylon 66 | PRL |
| CPI PP 40 Other | CPI Binani, Inc. | PP, Unspecified | CPI PP |
| Hanwha Total PE 610A | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LDPE | Hanwha Total PE |
| IROGRAN® A 95 E 4861 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| Petrothene® NA204000 (Extrusion Coating) | LyondellBasell Industries | LDPE | Petrothene® |