CERTENE™ HWB-554
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FsSa4p_CERTENE-HWB-554.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HWB-554 is a certified prime grade Hexene copolymer High Molecular Weight developed for BLOW MOLDING of high performance medium to large size industrial containers. HWB-554 features High-Swell, consistent processability, outstanding combination of ESCR, Impact strength, Stiffness, Creep resistance, and excellent chemical resistance. HWB-554 applications include 55 gallon drums, shipping containers, industrial tanks, agrochemicals, automotive parts, tool boxes, carrying cases, sport articles, ski and baggage car boxes. HWB-554 recommended processing temperature is 210 to 230°C.. HWB-554 complies with FDA regulation 21CFR 177.1520 (c) 3.2 (a) and with most international regulations concerning the use of Polyethylene in contact with food articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.954 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.028 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 5.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | |||
| Molding, F50 | > 1000 | hr | ASTM D1693 |
| 50°C, 1.75mm, 10% Igepal, molded, F50 1 | 45.0 | hr | ASTM D1693B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield, Compression Molded) | 26.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 800 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 4(Compression Molded) | 1170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength | 380 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 45.0 | °C | ASTM D648 |
| Brittleness Temperature | < -90.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 130 | °C | ASTM D1525 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blow Molding Temperature | 210 - 230 | °C | |
| Test specimens from compression molded plaque according to ASTM D 1928 Procedure C. |
| Note Message | |
|---|---|
| 1 . | Notched Bent Strip |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Therma-Tech™ TT3300-8701 EI FR | PolyOne Corporation | PBT | Therma-Tech™ |
| Verolloy B1400MM | PlastxWorld Inc. | ABS+PBT | Verolloy |
| Clearflex® H&T FHH 508 | Versalis S.p.A. | LMDPE | Clearflex® H&T |
| Electrafil® PVDF C BK | Techmer Engineered Solutions | PVDF | Electrafil® |
| Karina BLACK PVC COMPOUND -E 700D48/ 1-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |