Braskem PE SLH218
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FrG8Km_BraskemPESLH218.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: SLH218 is a LLDPE Hexene copolymer produced by Braskem. It shows a good balance between optical properties, mechanical properties (Mainly stretchability), sealability and processability. Very low gel contained. The minimum biobased content of this grade is 84%, determined according to ASTM D6866. Additive: Slip Absent Antiblock Absent Applications: Stretch films; Liners; LDPE and HDPE blends; packages for general use; Others applications: insulation for low and medium tension XLPE wires and cables; blends for irrigation pipes. Process: Cast Film Extrusion |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.916 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.3 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 38 µm | 40.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 40.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm | 1200 | % | ASTM D882 |
| TD : Fracture, 38 µm | 1500 | % | ASTM D882 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant, MD : 38 µm | 210 | MPa | ASTM D790 |
| 1% Secant, TD : 38 µm | 240 | MPa | ASTM D790 |
| Dart Drop Impact 1 | 110 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 240 | g | ASTM D1922 |
| TD : 38 µm | 520 | g | ASTM D1922 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 84 | % | ASTM D6866 |
| Extrusion instructions |
|---|
| Blown Films Extrusion Temperature Profile: from 150 to 250°C Screen Package: 40/40 - 100% pure 40/60/40 - Blend Mass Temperature: 230°C (max 260°C) |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Promyde® B25 | NUREL, S.A. | Nylon 6 | Promyde® |
| Sinkral® C 442 | Versalis S.p.A. | ABS | Sinkral® |
| UNINOR® PPO Modified | Nytef Plastics, Ltd. | PPE+PS | UNINOR® |
| DOW™ LDPE 410F | The Dow Chemical Company | LDPE | DOW™ LDPE |
| Haysite Plastics ETR-FR-C | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |