Grivory® HT2V-5H

Category:	Nylon 6T/66 , Polyamide 6T/66 Copolymer
Manufacturer:	EMS-GRIVORY
Trademark:	Grivory®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Fqxt8e_Grivory-HT2V-5H.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Grivory® HT2V-5H is a Polyamide 6T/66 Copolymer (Nylon 6T/66) material filled with 50% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding.

Important attributes of Grivory® HT2V-5H are:

Flame Rated

RoHS Compliant

Good UV Resistance

Heat Resistant

Typical applications include:

Automotive

Engineering/Industrial Parts

Household Applications

Outdoor Applications

Sporting Goods

General Information
Filler / Reinforcement	Glass Fiber, 50% Filler by Weight
Features	Good UV Resistance High Heat Resistance
Uses	Automotive Applications Automotive Exterior Parts Automotive Interior Parts Engineering Parts Household Goods Hydraulic Applications Outdoor Applications Pneumatic Applications Power/Other Tools Sporting Goods
RoHS Compliance	RoHS Compliant
Forms	Granules
Processing Method	Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Dry	Conditioned	Unit	Test Method
Density	1.62	--	g/cm³	ISO 1183
Molding Shrinkage				ISO 294-4
Across Flow	0.70	--	%
Flow	0.10	--	%
Water Absorption				ISO 62
Saturation, 23°C	3.5	--	%
Equilibrium, 23°C, 50% RH	1.2	--	%

Hardness	Dry	Conditioned	Unit	Test Method
Ball Indentation Hardness	325	325	MPa	ISO 2039-1

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	17500	17000	MPa	ISO 527-2
Tensile Stress (Break)	250	215	MPa	ISO 527-2
Tensile Strain (Break)	2.0	2.0	%	ISO 527-2

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	11	10	kJ/m²
23°C	11	11	kJ/m²
Charpy Unnotched Impact Strength				ISO 179/1eU
-30°C	60	60	kJ/m²
23°C	75	75	kJ/m²

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, Unannealed	280	--	°C	ISO 75-2/A
8.0 MPa, Unannealed	230	--	°C	ISO 75-2/C
Maximum Use Temperature				Internal Method
Long Term	140	--	°C
Short Term	240	--	°C

Additional Information	Dry	Conditioned		Test Method
ISO Type	PA6T/66, MH, 14-190, GF50	--		ISO 1874

Thermal	Dry	Conditioned	Unit	Test Method
Melting Temperature ¹	310	--	°C	ISO 11357-3
CLTE				ISO 11359-2
Flow	1.0E-5	--	cm/cm/°C
Transverse	5.5E-5	--	cm/cm/°C

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	--	1.0E+12	ohms	IEC 60093
Volume Resistivity	1.0E+12	1.0E+12	ohms·cm	IEC 60093
Electric Strength	38	38	kV/mm	IEC 60243-1
Comparative Tracking Index	--	600	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flammability Classification (0.800 mm)	HB	--		IEC 60695-11-10, -20

Note Message
1 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
POLYSTONE® Safe-Tec L	Röchling Engineering Plastics SE & Co. KG	TP, Unspecified	POLYSTONE®
SABIC® PPcompound 5521	SABIC Innovative Plastics	PP, Unspecified	SABIC® PPcompound
Moplen EP5001	PolyMirae	PP Copolymer	Moplen
Hapflex™ 661	Hapco Inc.	TP, Unspecified	Hapflex™
Kumho EP HAG 5220	Korea Kumho Petrochemical Co., Ltd.	ABS	Kumho EP