Smooth-Sil® 950
| Category: | Silicone , Silicone |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | Smooth-Sil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fqd9kN_Smooth-Sil-950.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Smooth-On Smooth-Sil® Platinum Silicones cure at room temperature with negligible shrinkage. With different hardnesses to choose from, Smooth-Sil® products offer tremendous versatility and are suitable for making production molds of any configuration, large or small. These silicones exhibit good chemical, abrasion and heat resistance. Materials such as plasters, concrete, wax, low-melt metal alloys or resins (urethane, epoxy or polyester) can then be cast into these silicone rubbers without a release agent. Smooth-Sil® Platinum Silicones are used for rapid prototyping, wax casting (foundries and candle makers), architectural restoration and for casting concrete. Smooth-Sil® 940 is suitable for food related applications. (See separate technical bulletin for usage instructions available at www.smooth-on.com). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D1475 |
| Specific Volume | 0.932 | cm³/g | ASTM D1475 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mixing Ratio | 100A:10B by weight | ||
| Operating Temperature | -54 to 232 | °C |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | < 0.010 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 50 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 1.88 | MPa | ASTM D412 |
| Tensile Strength (Break) | 5.00 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 320 | % | ASTM D412 |
| Tear Strength 1 | 27.1 | kN/m | ASTM D624 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | > 14 | kV/mm | ASTM D149 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life | 45 | min | ASTM D2471 |
| Thermoset Mix Viscosity | 35000 | cP | ASTM D2393 |
| Demold Time | 1400 | min |
| Note Message | |
|---|---|
| 1 . | Die B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRILAC® ABS-HF5500 | Polymer Technology and Services, LLC | ABS | TRILAC® |
| DOMAMID® A1-008-V30-H2-DB | DOMO Engineering Plastics GmbH | Nylon 6 | DOMAMID® |
| FORMULA P COMP 5220 | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| INSTRUC PPSLGF50 | Infinity LTL Engineered Compounds | PPS | INSTRUC |
| OXNILON 66 Moly | Oxford Polymers | Nylon 66 | OXNILON 66 |