Task® 9 Colormatch
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | Task® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FqW1bS_Task-9-Colormatch.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TASK® 9 Colormatch is a high performance urethane casting resin that features very high compressive strength and tensile strength. TASK® 9 is clear amber, which makes this plastic very easy to color using SO-Strong® or IGNITE® colorants. With a mix ratio of 1A:1B by volume, TASK® 9 is easy to use and a low mixed viscosity (300 cps) ensures minimal bubble entrapment. Pot life is 7 minutes and cure time is about 60 minutes (depending on mass). TASK® 9 is ideal for making impact resistant tooling, color accurate prototypes / models as well as durable reproductions. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D1475 |
| Specific Volume | 0.878 | cm³/g | ASTM D1475 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mixing Ratio | 1A:1B by volume |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow (23°C, 7 days) | 0.90 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2550 | MPa | ASTM D638 |
| Tensile Strength (Break) | 53.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength | 81.7 | MPa | ASTM D790 |
| Compressive Modulus | 676 | MPa | ASTM D695 |
| Compressive Strength | 75.8 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 55.0 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 7.0 | min | ASTM D2471 |
| Thermoset Mix Viscosity | 300 | cP | ASTM D2393 |
| Demold Time 1(23°C) | 60 | min |
| Note Message | |
|---|---|
| 1 . | Cure Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC G-2163 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| MTEGRITY™ HDPE HD300 | M. Holland Company | HDPE Copolymer | MTEGRITY™ HDPE |
| NatureFlex™ 400NPU | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| Desmovit® DP R 9924 | geba Kunststoffcompounds GmbH | TPU-Ester/Ether | Desmovit® |
| Hanwha Total PP HY301 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Homopolymer | Hanwha Total PP |