Celanex® 2104UV
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FqAg6m_Celanex-2104UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex 2104UV is an unreinforced, impact modified, UV stabilized PBT designed for outdoor agricultural, industrial and automotive applications. Celanex 2104UV is suitable for injection molding applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.31 | g/cm³ | ASTM D792 |
| -- | 1.26 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 75 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow | 1.8 - 2.0 | % | ASTM D955 |
| Vertical flow direction | 2.2 - 3.3 | % | ISO 294-4 |
| Flow direction | 2.2 - 3.3 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, 23°C | 57.2 | MPa | ASTM D638 |
| Yield | 46.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 250 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 2080 | MPa | ISO 178 |
| Flexural Stress (23°C) | 63.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.9 | kJ/m² | ISO 179/1eA |
| 23°C | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 130 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 224 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 130 | °C | ASTM D648 |
| Melting Temperature 1 | 225 | °C | ISO 11357-3, ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | 1.0E+16 | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| -- 2 | 17 | kV/mm | ASTM D149 |
| -- | 23 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 MHz | 3.20 | ASTM D150 | |
| 100 Hz | 4.00 | IEC 60250 | |
| 1 MHz | 3.50 | IEC 60250 | |
| Dissipation Factor | |||
| 1 MHz | 2.0E-3 | ASTM D150 | |
| 100 Hz | 7.0E-3 | IEC 60250 | |
| 1 MHz | 0.020 | IEC 60250 | |
| Comparative Tracking Index | > 600 | V | ASTM D3638 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 235 - 250 | °C | |
| Nozzle Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 65.0 - 96.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Manifold Temperature: 250 to 260°CZone 4 Temperature: 240 to 260°CFeed Temperature: 230 to 240°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4707 | RTP Company | PTT | RTP |
| SABIC® HDPE FI0750 | Saudi Basic Industries Corporation (SABIC) | HDPE, HMW | SABIC® HDPE |
| SCHULAMID® 66 GF 25 FR 5 | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Shanghai Potomer SG6 | Shanghai Potomer International Trade Co., Ltd. | PVC, Unspecified | Shanghai Potomer |
| Flexathene® TP4310HR | LyondellBasell Industries | Polyolefin, Unspecified | Flexathene® |