Ferro PP LPP20BN18HB-WH
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FppFSg_Ferro-PP-LPP20BN18HB-WH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ferro PP LPP20BN18HB-WH is a Polypropylene material filled with 20% calcium carbonate. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Ferro PP LPP20BN18HB-WH are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 29 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 71 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 24.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 60 | % | ASTM D638 |
| Flexural Modulus | 1520 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 37.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 910 | J/m | ASTM D256 |
| Gardner Impact | 11.3 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 98.9 | °C | |
| 1.8 MPa, Unannealed | 57.8 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 202 to 204 | °C | |
| Middle Temperature | 204 to 210 | °C | |
| Front Temperature | 210 to 213 | °C | |
| Nozzle Temperature | 213 to 218 | °C | |
| Mold Temperature | 43.3 to 51.7 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® F7870 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Sylvin 9077-95 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Baoding 76E85 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyether | Baoding |
| Clearflex® H&T CMH 108 | Versalis S.p.A. | LLDPE | Clearflex® H&T |
| PSM® HL-104 | Wuhan Huali Environmental Technology Co., Ltd. | TP, Unspecified | PSM® |