Petrothene® NA951000
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FpFgg2_Petrothene-NA951000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PETROTHENE NA951000 is specially designed for industrial and consumer packaging and liner and bag applications. NA951000 has an excellent balance of processability, toughness and drawdown and does not contain slip or antiblock. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.2 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(1.91 mm) | 13.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 1.91 mm) | 600 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| Secant Modulus | ASTM D882 | ||
| MD : 32 µm, Blown Film | 197 | MPa | |
| TD : 32 µm, Blown Film | 228 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm, Blown Film | 24.8 | MPa | |
| TD : Yield, 32 µm, Blown Film | 17.2 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 32 µm, Blown Film | 250 | % | |
| TD : Break, 32 µm, Blown Film | 520 | % | |
| Dart Drop Impact (32 µm, Blown Film) | 100 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm, Blown Film | 320 | g | |
| TD : 32 µm, Blown Film | 100 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 |
| Note Message | |
|---|---|
| 1 . | Type IV, 510 mm/min |
| 2 . | Type IV, 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC PG 58/K1-UV | Fainplast Compounds S.r.l | PVC+NBR | Fainplast PVC |
| POCAN® BFN 4211 000000 000000 | LANXESS Asia/Pacific | PBT | POCAN® |
| Politen® G3LS10 | ITEN INDUSTRIES | Polyester Alloy | Politen® |
| TOTAL Polyethylene Lumicene® M 4043 UV (EU) | TOTAL Refining & Chemicals | mMDPE | TOTAL Polyethylene |
| Vydyne® 65B | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |